Products Specification
Back Next
 
NIKAWA M118P is a high performance2-component epoxy adhesive with superior mechanical strength, excellent bonding strength to wood, concrete, fibreglass, ceramic, marble, metal and other surfaces. Extensively used in marine-timber and fibre boat manufacturing and maintenance.
   
 
Technical Properties
Part A Epoxy Binder (White Color)
Part B Hardener (Amber Color)
Mix Ratio A:B (By Volume) 1:1
Viscosity Paste
S.G. kg/litre 1.1-1.3
Pot Life (TECAM) 250gm @ 20©C Approx. 30 minutes
Cure Time at 20-25©C Minimum 24 hours
Hardening Condition 7 days at 20©C
Tensile Strength (ASTM C307) 24 N/mm²
Compressive Strength (BS 6319) 70-80 N/mm²
Tensile Strength in Flexure (Din 1164) 30-40 N/mm²
Peel Strength (Din 53282) 6-10 N/mm²
Coefficient of Linear Thermal Expansion 60.10-6/©C
Water Absorption (DIN 53475) 24h Cold 34mg

Chemical Resistance
Test Media
Rating
 Test Media
Rating
Dilute Acetic Acid
++
 Dilute Hydrochloric Acid
++
Dilute Sulphuric Acid
++
 Diluted Nitric Acid
++
Concentrate Acid
+
 Sdium Hydroxide
++
Ammonia
++
 Hydraulic Fluids
++
Diesel
++
 Mineral Oil
++
Salt Solution Concentrate
++
 Detergent
++
Water
++
 Toulene
++

Rating
++ Resistant
+ Limited Resistant
- Not Resistant

Surface Preparation:
All surfaces should be dried. cleaned and free from all contaminants.

Application:
Part A and B should be stirred before thoroughly mix until even color is achieved.

 
Back Next