Products Specification
Back Next
 
NIKAWA AB100 is a high performance 2 - component epoxy material, epoxy binder and hardener which consists of sand filler-in compound used bridge bearing pads, bedding concrete units, repairing structural concrete beams, sealing compounds, prefabricated concrete parts, etc. The mixture provides extremely high mechanical strength, chemical resistance and excellent bonding strength to conventional building materials.
   
 
Technical Properties:
Part A Epoxy Binder
Part B Hardener
Mix Ratio A:B (By Volume) 1:1
Viscosity of Mix Paste
S.G. kg/litre 1.9 - 2.0
Pot Life at 20©C Approx. 90 minutes
Cure Time at 20-25©C Minimum 24 hours
Hardening Condition 7 days at 20©C
Compressive Strength (BS 6319) 70-80 N/mm²
Tensile Strength in Flexure (Din 1164) 25-30 N/mm²
Coefficient of Linear Thermal Expansion 30.10-6/©C

Chemical Resistance:
Test Media
Rating
 Test Media
Rating
Dilute Acetic Acid
++
 Dilute Hydrochloric Acid
++
Dilute Sulphuric Acid
++
 Diluted Nitric Acid
++
Concentrate Acid
+
 Sdium Hydroxide
++
Ammonia
++
 Hydraulic Fluids
++
Diesel
++
 Mineral Oil
++
Salt Solution Concentrate
++
 Detergent
++
Water
++
 Toulene
++

Rating
++ Resistant
+ Limited Resistant
- Not Resistant

Surface Preparation:
-
All surfaces should be dried. cleaned and free from all contaminants.
-
New concrete surface must be fully cured.

Application:
-
Concrete surfaces to be treated with NIKAWA AB100 system should be primed with NIKAWA EPOXY PRIMER.
-
Part A and B should be stirred before thoroughly mix until even color is achieved.

Packaging:
Nika AB100: Part A - 6kg
Part B - 6kg

 